产品介绍：

HENRY 570用于砂浆地坪，混凝土基层加固，也可用于水泥基地坪密封加固。

 

特点：

●水性环保；
●无机小分子，渗透力超强；
●结晶封闭毛细孔，增强地坪强度。

 

适用场所：

用于地面吸收性基层如混凝土、水泥砂浆等，对于表面起砂的基层具有超强的渗透力，增强地坪强度，同时封闭基层的毛细孔和缝隙，降低多孔性基层的吸收性。

 

基层处理：

基层需具有多孔吸收性、平整、干燥、干净、无裂缝、无油渍、脱模剂等化学助剂。

 

技术参数：

颜色：                     无色透明
状态：                     液态
固含量：                  ≥20%
密度：                     约1.05kg/L
单耗：                     约100-150g/m²（用量仅供参考，因基层疏松状况而异）

 

施工方法：

1、清除地面表层不稳定松散物，油污等；

2、本加固剂不兑水或按照1：1-2兑水，用滚筒刷涂一遍，确保完全渗透；

3、待第一遍完全干燥后，涂刷第二遍，若希望得到更好的增强效果，可涂刷多遍。

 

注意事项：

适合在5℃-35℃气温下使用。基层需平整、干燥，施工前应清洁基层表面。本说明书提供的数据是在23℃±2℃气温下和50-55%的相对湿度下取得的。请注意，在其它气候环境下，干燥的时间会相应延长或缩短。

 

包装与储存：

20Kg塑料桶包装。本品须存于室内5℃-35℃，严防霜冻和曝晒，保质期为12个月。

 

 

 

HENRY570 Osmotic Crystallization Reinforcement

Uses:

Used for mortar floor, concrete base reinforcement, also can be used for inorganic grindstone floor sealing reinforcement.

Features:

Environmental protection;

Inorganic small molecules with super penetrability;

The crystallization closes the wool stoma, enhances the floor strength.

Technical parameters:

Color	Clear
State	Liquid
The solid content	≥20%
Density	About 1.05kg/L
Consumption	About 100-150g/ m2 (Dosage for reference, due to different levels of base loose condition)

 

Applicable interface:

Used for ground absorption base, such as concrete, cement mortar, etc., for the surface of the basic level of sand has super penetration, enhance floor strength, at the same time close the wool pores and gaps of the basic level, reduce the absorption of porous base.

Basic processing:

The base needs porous absorption, flat, dry, clean, no cracks, no oil stains, release agent and other chemical aids.

Application:

1. Remove unstable loose matter and oil stains on the surface of the ground.

2. This reinforcement agent does not add water or according to 1:1-2, with a roller brush to ensure complete penetration.

3. After the first time completely dry, paint brush second, if you want to get a better enhancement effect, can paint brush many times.

Notes:

HENRY570 is suitable for use at 5℃-35℃ air temperature. The base shall be flat and dry, and the surface of the base shall be cleaned before construction. The data provided in this manual are obtained at temperature of 23℃±2℃ and relative humidity of 50-55%.Please note that in other climates, drying time may be extended or shortened.

Packaging and storage:

20Kg/barrel. This product should be stored in the indoor 5℃-35℃, to prevent frost and solarization. Shelf life is 12 months.